Hauthane HD-2883 DMM
An NMP-free, APEO-free, polyester-based, hydroxyl-functional, aliphatic, water-borne polyurethane dispersion.
Suggested Uses: L-2883 was developed for use with water-dispersible, isocyanate crosslinkers such as Bayer’s Bayhydur 302 or Perstorp’s Easaqua X D 401. The product, when crosslinked provides tough, chemical-resistant, semi-gloss coatings which may be applied to a variety of substrates including concrete, metals, plastics and wood materials.
Characteristics:
- Superior chemical resistance
- Excellent exterior weathering durability
- Excellent humidity resistance
- Contains dipropylene glycol dimethyl ether co-solvent
Physical Properties
Solids | 35 % |
Solids Tolerance | ± 1 % |
Viscosity | 50 to 500 cps |
pH | 7.5 to 10.0 |
Density | 8.8 lb/gal |
Volatile Organic Compounds (VOC) Content (As Supplied) | 70 g/L |
OH Equivalent Weight (As supplied) | 3100 |
Sward Hardness | 44 |
Tensile Properties
Elongation | 230 % |
Tensile Strength | 7000 psi |
100 % Modulus | 4850 psi |
200 % Modulus | 6800 psi |
Note | Tested at 20 inches/minute |
Application
L-2883 crosslinked with water-dispersible isocyanates may be spray applied using single-component equipment. The workable potlife is approximately 3 hours at the suggested crosslinker ratio of 2.0 to 1.0 NCO / OH.
Curing
L-2883, crosslinked with a water dispersible isocyanate, will dry to a hard film in 30 minutes at ambient room temperature (65 – 70 ºF) and humidity (RH 50 %). Ultimate cured properties will take 3 – 5 days to develop. If heat is available, the ultimate properties can be attained in shorter time. Typical oven drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties.